Strength | 10.9 | 12.9 | Clause | Existing |
---|---|---|---|---|
Strength Quality | BORON steel | SCM435 | Type | A2 |
Hardness | 32 ~ 39 | 39 ~ 44 | Strength Quality | STS304 |
Note |
Nickel plating Black oxide |
Nickel plating Electroless Nickel plating Black oxide |
the title of screw(d) | the pitch of a screw(P) | s | spring washer |
plain washer (internal diameter X external diameter X thickness) |
a(Max) | ||||
---|---|---|---|---|---|---|---|---|---|
Title (Reference Dimensions) |
Min | Max | S+P/W | S/W | P/W | ||||
M3 | 0.5 | 2.5 | 2.52 | 2.58 | ∮2.7 | 2.8 X 6 X 0.6 | 3.0 | 2.4 | 1.5 |
M4 | 0.7 | 3 | 3.02 | 3.08 | ∮3.6 | 3.7 X 8 X 0.8 | 4.4 | 3.5 | 2.3 |
M5 | 0.8 | 4 | 4.02 | 4.095 | ∮4.6 | 4.6 X 10 X 10 | 5.4 | 4.3 | 2.7 |
M6 | 1 | 5 | 5.02 | 5.14 | ∮5.5 | 5.6 X 12.5 X 1.6 | 6.9 | 5.1 | 3.7 |
M8 | 1.25 | 6 | 6.02 | 6.14 | ∮7.4 | 7.4 X 17 X 1.6 | 8.4 | 6.7 | 4.2 |
M10 | 1.5 | 8 | 8.025 | 8.175 | ∮9.4 | 9.5 X 21 X 2.0 | 10.4 | 8.2 | 5.2 |
Clause Num |
Mechanical and physical properties | Strength classification | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
3.6 | 4.6 | 4.8 | 5.6 | 5.8 | 6.8 | 8.8 | 9.8 | 10.9 | 12.9 | |||||
d≤16mm | d>16mm | |||||||||||||
5.1 |
Tensile strength Rm, nom N/mm² |
300 | 400 | 500 | 600 | 800 | 800 | 900 | 1000 | 1200 | ||||
5.2 |
Minimum tensile strength Rm, min N/mm²(kgf/mm²) |
330 | 400 | 420 | 500 | 520 | 600 |
800 (81.6) |
830 (84.6) |
900 |
1040 (106) |
1220 (124) |
||
5.3 | Vickers Scale(Hv) | Min | 95 | 120 | 130 | 155 | 160 | 190 | 250 | 255 | 290 | 320 | 385 | |
F≥30 D² | Max | 220 | 250 | 320 | 335 | 360 | 380 | 435 | ||||||
5.4 | Brinell hardness(HB) | Min | 90 | 114 | 124 | 147 | 152 | 181 | 238 | 242 | 276 | 304 | 366 | |
F=30 D² | Max | 209 | 238 | 304 | 318 | 342 | 361 | 414 | ||||||
5.5 | Rockwell scale(HRC) | Min | - | - | - | - | - | - | 22 | 23 | 28 | 32 | 39 | |
Max | - | - | - | - | - | - | 32 | 34 | 37 | 39 | 44 | |||
5.6 | Surface hardness HV 0.3 | Max | - | 320 | 356 | 380 | 402 | 454 | ||||||
5.7 | down yield stress | title | 180 | 240 | 320 | 300 | 400 | 480 | - | - | - | - | - | |
ReL N/mm² | Min | 190 | 240 | 340 | 300 | 420 | 480 | - | - | - | - | - | ||
5.8 | 0.2% proof stress | title | - | 640 | 640 | 720 | 900 | 1080 | ||||||
Rp0.2 N/mm² | Min | - | 640 | 660 | 720 | 940 | 1100 | |||||||
5.9 |
Proof load stress Sp Sp/ReL or Sp/Rp0.2 N/mm² |
0.94 | 0.94 | 0.91 | 0.93 | 0.90 | 0.92 | 0.91 | 0.91 | 0.90 | 0.88 | 0.88 | ||
180 | 225 | 310 | 280 | 380 | 440 | 580 | 600 | 650 | 830 | 970 | ||||
5.10 | Breaking torque MB | Nm Min | - | 59.2 | 61.2 | 66.3 | 84.5 | 98.9 | ||||||
5.11 | Fracture Elongation A | Min | - | - | - | - | - | - | 12 | 12 | 10 | 9 | 8 | |
5.12 | Breaking torque Z | % Min | - | 52 | 48 | 48 | 44 | |||||||
5.13 | Wedge tensile test | The value of the full-size bolts and screws (not studs) must be greater than or equal to the minimum value for the longest strength (see 5.2). | ||||||||||||
5.14 | impulse strength KU | J Min | - | 25 | - | 30 | 30 | 25 | 20 | 15 | ||||
5.15 | Head impact strength | It must not be destroyed. | ||||||||||||
5.16 | Minimum height of non-carburized screws, E | - | ½H1 | ⅔H1 | ¾H1 | |||||||||
Maximum height of completely decarburized area, G mm | - | 0.015 | ||||||||||||
5.17 | Hardness after tempering | - | The value of the Vickers hardness should not decrease by more than 20. | |||||||||||
5.18 | urface flaw | Satisfy ISO 6157-1 (KSB 0547) or ISO 6157-3 (KSB 0549) |